LL0209AF
LLDPE for Film Application
LL0209AF is a linear low-density polyethylene copolymer with Butene-1 as the comonomer. It is intended for wide range of blown film applications, which offers superior hot-tack performance and higher tensile strength. LL0209AF contains process aid to allow easier extrusion; thus, preventing melt fracture.
APPLICATIONS
- Laminating Films
- Carrier and Garbage Bags
- Sealing Layers
- Industrial Bags
| PHYSICAL PROPERTIES |
TEST REFERENCE |
UNIT |
TYPICAL VALUE1 |
| MFI, 190°C/ 2.16 |
ASTM D 1238-98 |
g/10min |
1.0 |
| Density, non-annealed |
ASTM D 1505-98 |
g/cm³ |
0.920 |
| MECHANICAL PROPERTIES |
| Dart Impact Strength |
ISO 6603/1-1985 |
g |
160 |
| Tensile Stress at Yield MD/TD |
ISO 1184-1983 |
MPa |
11/12 |
| Tensile Strength at Break MD/TD |
ISO 1184-1983 |
MPa |
40/31 |
| Elongation at Break MD/TD |
ISO 1184-1983 |
MPa |
650/850 |
| Elmendorf Tear Strength MD/TD |
ISO 6383/2-1983 |
N |
2.4/6.0 |
| Coefficient of Friction |
ISO 8295-1986 |
- |
>0.50 |
| Haze |
ASTM D 1003-1991 |
% |
12 |
| Gloss (45°) |
ASTM D 2457-1990 |
% |
50 |
| THERMAL PROPERTIES |
| Melting Point |
ASTM D 2117 |
°C |
122 |
| ADDITIVES: ANTIOXIDANT , PROCESS AID |
1Film extruded at 2:1 blow ratio and 38 microns. MD = Machine Direction TD = Traverse Direction
2Typical value should not be construed as specification limits. They are intended to serve as guide only.
For Additional Information and Technical Assistance: